Sweet Corrosion Inhibition by CO2 Capture


Jesus Porcayo-Calderon 1,*

, Jorge Canto 2, L. M. Martinez-de-la-Escalera 2 and Adrian Neri 2

Citation: Porcayo-Calderon, J.; Canto, J.; Martinez-de-la-Escalera, L.M.; Neri, A. Sweet Corrosion Inhibition by CO2 Capture. Molecules 2022, 27, 5209. https://doi.org/10.3390/ molecules27165209

Academic Editor: Ioana Demetrescu

Received: 26 June 2022 Accepted: 25 July 2022 Published: 16 August 2022

Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affil- iations.

Copyright: © 2022 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https:// creativecommons.org/licenses/by/ 4.0/).

1 2

Abstract: The most practical and economical way to combat the problems derived from CO2 corrosion (sweet corrosion) is the use of corrosion inhibitors of organic origin. Its main protection mechanism is based on its ability to adsorb on the metal surface, forming a barrier between the metal surface and the aggressive medium. However, despite its excellent performance, its inhibition efficiency can be compromised with the increase in temperature as well as the shear stresses. In this study, the use of an inorganic inhibitor is proposed that has not been considered as an inhibitor of sweet corrosion. The reported studies are based on using LaCl3 as a corrosion inhibitor. Its behavior was evaluated on 1018 carbon steel using electrochemical measurements, such as potentiodynamic polarization curves, open-circuit potential measurements, linear polarization resistance measurements, and electrochemical impedance. The results showed an inhibition efficiency of the sweet corrosion process greater than 95%, and that the inhibition mechanism was different from the classic corrosion process in CO2-free electrolytes. In this case, it was observed that the inhibitory capacity of the La3+ cations is based on a CO2-capture process and the precipitation of a barrier layer of lanthanum carbonate (La2 (CO3 )3 ).

Keywords: corrosion; CO2 capture; lanthanum chloride; lanthanum carbonate; inhibitor

1. Introduction

CO2 corrosion is one of the main causes of the degradation of metallic materials in the oil industry and is the cause of significant environmental damage, as well as economic damage due to the unavailability of equipment. This degradation process is a surface process that encouraged an in-depth study of the mechanisms of metallic dissolution [1–3] as well as how to mitigate it.

The degradation of materials by dissolved CO2, also known as sweet corrosion, is a process that causes damage to the internal surface of the pipelines used in the transportation of hydrocarbons. This type of damage is also known as internal corrosion. The pipelines used to transport hydrocarbons are made of carbon steel, where its main element (Fe) has a standard potential that places it as a highly active element in acid conditions. Although carbon steel can protect itself due to the precipitation on its surface of a layer of iron carbonate (FeCO3), the conditions for this to occur are environments of high temperature, alkaline pH, and high concentration of Fe2+ cations [3–5], in addition to the high availability of dissolved CO2. However, the high concentration of Fe2+ cations implies an advanced corrosion process so that self-sealing can occur.

Due to the impossibility of carrying out a continuous inspection to determine the internal surface state, one of the main actions used to inhibit the metal dissolution process has been the injection of corrosion inhibitors into the corrosive fluid. These compounds can form protective layers on the metal surface, either by absorption or precipitation. Most corrosion inhibitors are organic compounds, and in their structure, they contain nitrogen (N), sulfur (S), and oxygen (O) atoms, unsaturated functional groups, as well as aromatic rings that favor their adsorption on the metal surface, due to a lone pair of electrons [6–11]. Corrosion inhibitors can reduce metal dissolution by at least 90% when they are added

Department of Chemical Engineering and Metallurgy, University of Sonora, Hermosillo 83000, Mexico

Corrosion y Proteccion (CyP), Buffon 46, Mexico City 11590, Mexico * Correspondence: jporcayoc@gmail.com

   

Molecules 2022, 27, 5209. https://doi.org/10.3390/molecules27165209 https://www.mdpi.com/journal/molecules

Molecules 2022, 27, 5209

2 of 18

to the electrolyte in doses as low as ppm. However, it has been reported [12–14] that its inhibition efficiency decreases with increasing temperature.

In recent decades, there has been great interest in using rare earth elements to syn- thesize compounds with corrosion inhibitory capacity in aggressive environments [15–25]. Its excellent corrosion inhibiting ability has been attributed to the high reactivity of rare earth. During the electrochemical corrosion process, the cathodic reaction activates the O2 reduction reaction, causing an increase in pH at the cathodic sites [22]. These con- ditions favor the precipitation of rare earth ions on the metal surface, forming a protec- tive film that decreases the cathodic reaction rate and, therefore, the corrosion current density [16,18,19,22,26,27].

Based on the above, the objective of this research work is to study the effect of an inorganic compound (LaCl3) on the corrosion behavior of carbon steel in a solution of NaCl (3.5% by weight) saturated with CO2 at 60 ◦C. LaCl3 can be considered a safe com- pound since its toxicity is similar to that of NaCl [16,27,28], and to date, it has not been considered a corrosion inhibitor in environments with dissolved CO2. The test temperature was chosen to reference the experimental conditions under which the performance of corrosion inhibitors with potential use in pipelines used to transport hydrocarbons is eval- uated. The average temperature of the transported fluid is 50–60 ◦C [7–10]. The inhibitory capacity of LaCl3 was determined through electrochemical studies, such as polarization curves, measurements of open circuit potential, polarization resistance, and electrochem- ical impedance, as well as complementary analyses using scanning electron microscopy techniques (SEM-EDS) and X-ray diffraction.

2. Results and Discussion

2.1. Potentiodynamic Polarization Curves

Figure 1 shows the potentiodynamic polarization curves of carbon steel 1018 after 50 h of immersion in a 3.5% NaCl solution saturated with CO2 at 60 ◦C with and without the addition of LaCl3 as a corrosion inhibitor.

Figure 1. Polarization curves for 1018 carbon steel in CO2-saturated brine at different concentrations of lanthanum chloride after 50 h of immersion.

In the absence of a corrosion inhibitor, the oxidation reaction of Fe determines the behavior of the anodic branch. The observed anodic behavior corresponds to that sug-

Molecules 2022, 27, 5209

3 of 18

gested by increasing the polarization of the anodic branch [3,29]—that is, initially an active dissolution behavior followed by a transition behavior, a pre-passive behavior, and finally a passive state. The extension of these zones depends on the electrolyte composition where the Fe is immersed.

The addition of the inhibitor caused the displacement of the polarization curves to- wards lower corrosion densities and slightly nobler potentials. A decrease in the cathodic current density and the development of a pseudo-passive zone in the anodic branch are noticeable. These changes suggest that the presence of La3+ ions caused a decrease in both the anodic and cathodic reaction rates, possibly due to the development of a La-based pro- tective film on the metal surface. In the scientific literature, there is little information on the use of t rare earth or their compounds as corrosion inhibitors in electrolytes with dissolved CO2. The use of organic Pr compounds as corrosion inhibitors has been reported [30], and an increase in corrosion potential and an effect on both the anodic and cathodic branches have also been indicated. The observed behavior corresponds to a mixed-type inhibition; similar behavior has been reported with the addition of compounds based on rare earth in environments rich in chlorides [16–18,23,24].

Table 1 shows the values of the electrochemical parameters obtained from the Tafel zones of the potentiodynamic polarization curves (Figure 1).

Table 1. Electrochemical parameters of the polarization curves.

LaCl3 Ecorr (mM) (mV)

0 −740 0.1 −742 0.5 −744 1.0 −733 5.0 −722

ba bc (mv/Dec) (mV/Dec)

46 379 112 363 174 204 176 228 131 244

Icorr (mA/cm2 )

0.158 0.099 0.052 0.013 0.031

In the absence of an inhibitor, it was observed that the anodic slope is of the same order as those reported for metal dissolution processes exclusively [4], and its value is in good agreement with that obtained by the expression (46 mVexp vs. 44 mVcalc) [3]:

ba = 2.303RT , (1) (1+β)F

where R is the gas constant, T is the temperature (K), β is the symmetry coefficient (β = 0.5), and F is the Faraday constant. This suggests that even after 50 h of immersion in the electrolyte, the carbon steel was not able to develop a protective layer on its surface. The decrease in current density observed in the anodic branch between −685 and −650 mV may correspond to the precipitation of an amorphous colloid (FeCO3/Fe(HCO3)2) due to the supersaturation of Fe2+ ions, as has been suggested in other studies [4].

It is observed that at inhibitor concentrations less than 1.0 mM, the corrosion potential remains practically constant, and at concentrations greater than 0.5 mM, the corrosion potential shifts slightly towards the noble direction. Similarly, in the presence of the inhibitor, the slope of the anodic branch increases, which indicates a decrease in the rate of metal dissolution. On the contrary, in general, the slope of the cathodic branch decreased, possibly due to a decrease in the cathodic sites that caused a decrease in the rate of the cathodic reaction. It has been suggested that when the Tafel slope changes and does not follow a trend according to the concentration of the added inhibitor, it simply acts as a barrier reducing the reaction area [10]. The Icorr decreased, up to an order of magnitude, with increasing inhibitor concentration up to 1.0 mM, and at higher concentrations, it tends to increase slightly. The increase in Icorr values at concentrations greater than 1.0 mM may be due to the increase in Cl− ion concentration due to the addition of the inhibitor (LaCl3) [18,23,24]. The few reported studies indicate that the decrease in the corrosion rate

Molecules 2022, 27, 5209

4 of 18

due to the addition of compounds based on rare earth is greater in environments saturated by CO2 than in aerated environments, possibly due to the formation of different protective films [30].

2.2. Open Circuit Potential Measurements

Figure 2 shows the variation in OCP values for 1018 carbon steel during 50 h of immersion in a 3.5% NaCl solution saturated with CO2 at 60 ◦C with and without the addition of LaCl3 as a corrosion inhibitor.

Figure 2. Evolution of OCP values for 1018 carbon steel in CO2-saturated brine at different concentra- tions of lanthanum chloride.

In the absence of an inhibitor, carbon steel showed an increase in its OCP values up to the first 10 h of immersion, and subsequently, its values tended to increase slowly until reaching a steady state at the end of the test. In this case, the observed trend may correspond to the formation and accumulation of corrosion products on steel surfaces. On the other hand, in the presence of the inhibitor, in all cases after its addition, a sudden increase in OCP values was observed, followed immediately by a slight decrease. Subsequently, a slow increase in OCP values was observed until reaching the steady state after 10 h of immersion.

In general, abrupt changes in the OCP values have been associated with a reduction or increase in the rate of the anodic and/or cathodic processes [16,17]. In particular, the shifts to more active potentials, in addition to indicating an increase in the metal dissolution rate, also suggest a process of inhibition of the cathodic reaction [16], such as that observed with the use of compounds based on rare earth as corrosion inhibitors in solutions rich in chlorides [16,23,24,31]. This suggests that in solutions rich in chlorides saturated with CO2, the mechanism of inhibition of rare earth is different from that observed in the absence of CO2.

The sudden increase in OCP values may be associated with a change in solution chemistry and/or the formation and partial dissolution of a protective film on the steel surface. Notwithstanding the evident shift in OCP values, the magnitude of the shift is less than 85 mV, and this suggests that lanthanum chloride acts as a mixed inhibitor [32,33].

2.3. Linear Polarization Resistance Measurements

Figure 3 shows the variation in polarization resistance values for carbon steel 1018 during 50 h of immersion in a 3.5% NaCl solution saturated with CO2 at 60 ◦C with and without the addition of LaCl3 as a corrosion inhibitor.

Molecules 2022, 27, 5209

5 of 18

Figure 3. Evolution of polarization resistance values for 1018 carbon steel in CO2-saturated brine at different concentrations of lanthanum chloride.

In the absence of an inhibitor, carbon steel showed a rapid increase in its Rp values in the first 10 h of immersion, and subsequently, the trend is maintained but at a slower rate until the end of the test. The observed trend may correspond to a rapid corrosion process and accumulation of corrosion products on the steel surface, which limited the available reaction area. However, in the presence of the inhibitor, a similar behavior was observed regardless of its concentration. In all cases, immediately after the addition of the inhibitor, an abrupt increase in Rp values was observed, followed by an abrupt decrease. After this behavior, the Rp values tended to increase rapidly until 10 h of immersion, and then a constant increase was observed until the end of the test. The initial behavior is consistent with that observed with the OCP values (Figure 2).

This new evidence suggests that the addition of the inhibitor may have caused an instantaneous disturbance in the chemical composition of the solution, thereby causing a temporary decrease in its corrosivity. The magnitude of the Rp values is consistent with the Icorr values observed with the polarization curves (Figure 1); that is, the Rp values increase with the concentration of the inhibitor up to 1.0 mM, and at higher concentrations, they tend to decrease, possibly due to the increase in the concentration of Cl− ions [18,23,24].

Figure 4 shows the variation in the inhibition efficiency of LaCl3 as a function of its concentration for carbon steel immersed in a 3.5% NaCl solution saturated with CO2 for 50 h. The calculations show that the inhibition efficiencies are greater than 95% for concentrations up to 5 mM. At higher concentrations, it tends to decrease, possibly due to the increase in the concentration of Cl− ions. The maximum inhibition efficiency was 98% for a concentration of 1 mM of LaCl3. The results show that LaCl3 is a more efficient corrosion inhibitor in environments rich in chlorides saturated by CO2 than in the absence of CO2 [23,24], possibly because its protective action is different.

Molecules 2022, 27, 5209

6 of 18

Figure 4. Effect of LaCl3 concentration on inhibition efficiency. 2.4. Electrochemical Impedance Spectroscopy Measurements

Figure 5 shows the Nyquist and Bode diagrams for carbon steel after 50 h of immersion in a 3.5% NaCl solution saturated with CO2 at 60 ◦C with and without the addition of LaCl3 as a corrosion inhibitor.

From the impedance spectra, it is observed that all the spectra show similar behavior. The Nyquist diagram shows the apparent presence of a single capacitive semicircle whose maximum diameter is obtained for an inhibitor concentration of 1 mM. From the Bode plot in its impedance modulus format, the presence of the high and low-frequency plateau is observed, as well as a linear log f-log |Z| relationship in the intermediate frequency region. The evolution of the low-frequency plateau is consistent with the magnitude of the diameter of the capacitive semicircles. From the Bode plot in its phase angle format, the presence of only one time constant is confirmed in all cases. However, in the presence of an inhibitor, the magnitude of the phase angle is bigger, and its location is at higher frequencies than that observed in the absence of an inhibitor.

Figure 5. Cont.

Molecules 2022, 27, 5209

7 of 18

Figure 5. Nyquist and Bode diagrams for 1018 carbon steel in CO2-saturated brine at different concentrations of lanthanum chloride after 50 h of immersion. (a) Nyquist diagram; (b) Bode diagram in its impedance modulus format; (c) Bode diagram in its phase angle format.

Since in the presence of the inhibitor, the impedance spectra showed a similar evolu- tion, in subsequent analyses, only the evolution of the spectra in the absence (Figure 6) and presence of the inhibitor at a single concentration, 1 mM LaCl3 (Figure 7) is presented.

Molecules 2022, 27, 5209 8 of 18

Figure 6. Evolution of Nyquist and Bode diagrams for 1018 steel in CO2-saturated brine at 60 ◦C. (a) Nyquist diagram; (b) Bode diagram in its impedance modulus format; (c) Bode diagram in its phase angle format.

Molecules 2022, 27, 5209 9 of 18

Figure 7. Evolution of Nyquist and Bode diagrams for 1018 carbon steel in CO2-saturated brine at 60 ◦C and 1 mM of LaCl3. (a) Nyquist diagram; (b) Bode diagram in its impedance modulus format; (c) Bode diagram in its phase angle format.

Molecules 2022, 27, 5209

10 of 18

The evolution of the impedance spectra for the case of carbon steel in the absence of an inhibitor based on the Nyquist diagram shows the presence of a depressed capacitive semicircle, whose diameter increases as a function of immersion time. Data scatter in the low-frequency region has been associated with inhomogeneity and microroughness of the working electrode surface [11,34,35]. From the Bode plot in its impedance modulus format, |Z|, in the high-frequency region, the presence of the high-frequency plateau from 1000 Hz is observed, as well as the development of a linear relationship, log |Z|-log f, which extends to the low-frequency region as a function of time. In addition, in the low- frequency region, the presence of the low-frequency plateau is observed, the length of which decreases and moves to higher impedance modulus values with immersion time. From the Bode plot in its phase angle format, the presence of a time constant is visible, which shifts towards lower frequencies (80 Hz → 5 Hz) as a function of the immersion time, in addition, its maximum phase angle increases in the same way (55◦ → 67◦). The characteristics observed are congruent with a material whose surface forms a layer of corrosion products with protective characteristics.

However, after the corrosion test, the surface characteristics of the carbon steel (Figure 8) showed the accumulation of a thin layer of corrosion products. Under it, a hetero- geneous attack with the presence of pitting was observed. Then, the increase in the diameter of the capacitive semicircle, impedance module and phase angle may be associated with the accumulation of a porous layer of corrosion products that decreased the reaction area but not the corrosion process [19].

Figure 8. The morphological aspect of 1018 carbon steel after corrosion test in CO2-saturated brine solution after 50 h: (a) corrosion products surface; (b) clean surface.

In this type of environment, the main corrosion product with protected characteristics that develop on the surface of carbon steel is iron carbonate, FeCO3. However, the XRD analysis performed on the surface of the samples (Figure 9) did not detect their presence. This is because its formation is favored at higher temperatures and longer immersion times than those evaluated here [36]. In this case, the main corrosion product detected was Fe3O4.

Molecules 2022, 27, 5209

11 of 18

Figure 9. X-ray diffraction pattern of the surface of 1018 carbon steel; (a) not corroded, (b) corroded, (c) corroded with the addition of LaCl3.

In general, the corrosion process of carbon steel in deaerated conditions is due to the following anodic and cathodic reactions:

Fe ↔ Fe2+ + 2e−, (2) 2H+ + 2e− ↔ H2, (3)

During the active dissolution process, the Fe2+ cations can participate in secondary reactions that favor the formation of corrosion products, which can act as a barrier to the free access of the electrolyte and, with it, a reduction in the rate of metal dissolution.

Fe2+ + 2OH− ↔ Fe(OH)2 + H2O, (4)

4Fe(OH)2 + O2 + 2H2O ↔ 4Fe(OH)3, (5) 4Fe(OH)2 + O2 ↔ 2Fe2O3 + 4H2O, (6) Fe(OH)3 + O2 ↔ FeOOH + H2O, (7) 4Fe(OH)2 + O2 ↔ 4FeOOH + 2H2O, (8) 2FeOOH + H2O ↔ Fe2O3 + H2O, (9)

On the other hand, the evolution of the impedance spectra in the presence of the inhibitor (in the entire range of concentrations) presented a behavior like that shown in Figure 7. From the Nyquist diagram, the presence of a capacitive semicircle whose diameter increases with immersion time is shown. The magnitude of the diameter increase is greater than that observed in the absence of the inhibitor. From the Bode plot in its impedance modulus format, |Z|, the formation of the high-frequency plateau was observed from 1000 Hz, and in the intermediate frequency region, a linear relationship, log |Z|-log f, with only one slope was observed. In the low-frequency region, the presence of the low- frequency plateau was observed, which moves to higher impedance modulus values as a function of time. The magnitude of its displacement is greater than that observed in the absence of the inhibitor. From the Bode plot in its phase angle format, the presence of a single time constant is visible, which shifts towards lower frequencies (80 → 20 Hz) and increases its maximum phase angle (55◦ → 78◦) as a function of time. The magnitude

Molecules 2022, 27, 5209

12 of 18

of this shift was less than in the absence of an inhibitor, and the increase in phase angle maximum was greater. These characteristics suggest the formation of a thicker protective layer with higher capacitive properties than that formed in the absence of the inhibitor.

The surface characteristics of the carbon steel (Figure 10) after the corrosion test showed the presence of precipitates whose appearance changes depending on the concentration of the added inhibitor. At low concentrations (0.1 mM), a surface with a layer of reaction products of dense appearance was observed; when increasing the concentration (1.0 mM), the formation of structures that resemble the chrysanthemum flower was observed, and at higher concentrations (10.0 mM), the precipitates were different in shape and of higher density. To observe the appearance of the surface, the precipitates formed were removed by immersion in a HCl solution (10% v/v) for 5–10 s. The removal of the superficial layers showed that at low concentrations of the inhibitor, a more homogeneous surface was obtained than that observed in the absence of the inhibitor, and when increasing its concentration, scratch marks of the surface preparation were still observed. However, in the evaluation of the highest concentration of the inhibitor, an irregular surface with the presence of firmly adhered remnant deposits was observed, possibly due to the increase in the concentration of Cl− ions due to the addition of the inhibitor.

An EDS analysis and element mapping (Figure 11) revealed that the formed deposits are associated with La-O-C and that over the areas where the bulky deposits did not form, there was also this type of compound in the form of thin films.

Figure 10. Cont.

Molecules 2022, 27, 5209

13 of 18

Figure 10. The morphological aspect of 1018 carbon steel after corrosion test in CO2-saturated brine solution at different concentrations of the added inhibitor. 0.1 mM; (a) corrosion products surface; (b) clean surface. 1.0 mM; (c) corrosion products surface; (d) clean surface. 10.0 mM; (e) corrosion products surface; (f) clean surface.

XRD analysis of the carbon steel surface (Figure 9) showed that the precipitated La-O-C compound corresponds to lanthanum carbonate (La2(CO3)3). Regardless of the concentration of the inhibitor, lanthanum carbonate was the main compound detected in all cases. Its presence is associated with dissolved CO2 and La3+ cations, the product of inhibitor dissociation. Then, the increase in the diameter of the capacitive semicircle, impedance module and phase angle corresponds to the precipitation of this compound, which acted as a barrier layer between the metallic surface and the electrolyte.

Figure 11. Cont.

Molecules 2022, 27, 5209

14 of 18

 

Figure 11. Approach to the surface of 1018 carbon steel evaluated with the addition of 1.0 mM of LaCl3. (a) secondary electron image; (b) Fe mapping; (c) O mapping; (d) C mapping; (e) La mapping.

2.5. CO2-Capture and Protection Mechanism

Unlike the multiple corrosion studies in CO2-free electrolytes where it has been re- ported that the protection mechanism of rare earth is due to their precipitation (as oxides and hydroxides) by hydrolysis reactions of their metallic cations with the OH− ions pro- duced in the cathodic sites [19,23–25,37–40], a different mechanism was observed in this study, namely, CO2 capture and precipitation of lanthanum carbonate (La2(CO3)3) as a protective barrier.

Recent studies [41] indicate that in environments with CO2, the formation of rare earth carbonates, Ln2(CO3)3, is thermodynamically more favorable than species such as Ln(OH)3, Ln2O3, Ln(OH)−4, and even Ln3+. This is because its free energy of formation (∆G°f) is considerably more favorable. This indicates that lanthanum carbonates are more stable species, and therefore their protective capacity is greater. In addition, it is reported that the formation of rare earth carbonates is more favorable in aqueous systems with available carbonate ions (CO2−3) and that this mechanism corresponds to a CO2 capture process, where the CO2 capture efficiency is more than 95% [42].

Based on the above, the behavior observed in the OCP and RPL measurements can be justified, that is, the abrupt increase in both the open circuit potential and the polarization resistance when LaCl3 was added. A rapid capture process of the dissolved CO2 present in the vicinity of the metal surface occurred, thereby reducing the corrosivity of the electrolyte. The subsequent increase in these parameters (OCP, LPR) was a consequence of the constant bubbling of CO2, which restored its concentration. Because the CO2 hydration process is a slow step [3,5], the restoration of OCP and RPL values did not occur instantaneously. These sudden changes show the high reactivity of the La3+ cations, which offers a significant advantage over organic inhibitors. Under real conditions, it has been observed that the maximum effectiveness of organic inhibitors is detected up to two months after continuous injection. [43]

The capture process of CO2 and its precipitation as lanthanum carbonate can be explained according to the following reactions [41]:

LaCl3 ↔ La3+ + 3Cl− , (10) (s) (aq) (aq)

CO2(g) + H2O(l) ↔ H2CO3(aq) , (11) H2CO3(aq) ↔HCO3− +H+(aq), (12)

(aq)HCO− ↔CO2− +H+ , (13)

3(aq)

2La3+ + 3CO2− (aq) 3(aq)

3(aq) (aq)

↔ La2(CO3) , (14) 3(s)

Molecules 2022, 27, 5209

15 of 18

During the metal dissolution process, the dissociation reaction of carbonic acid (H2CO3), responsible for the formation of the electrochemically active species (H+) that buffers the concentration of hydrogen ions on the metal surface [1,2], favors the formation of carbonate ions and with it the precipitation reaction of lanthanum carbonate. However, because carbonic acid is a weak diprotic acid, it has been suggested that the first dissoci- ation step is a fast process, and the second is a slow process favored around neutral pH. Therefore, it is possible that the precipitation of lanthanum carbonate can also occur in a similar way to the precipitation reaction of iron carbonate in acid environments [5]:

2La3+ + 3HCO− ↔ La2(HCO3) , (15) (aq) 3(aq) 3(s)

La2(HCO3)3(s) ↔ La2(CO3)3(s) + 3H+, (16)

The hydration and dissociation reactions of the dissolved CO2 are reactions inherent in the classic mechanism of the sweet corrosion process [1–3], and in this case, the presence of the La3+ cations interrupt this route by capturing the dissolved CO2, thereby reducing the corrosivity of the electrolyte, and increases the corrosion resistance of the steel by forming a protective layer of La2(CO3)3 on its surface.

The source of cations for the formation of these carbonates does not depend on the Fe2+ cations generated during the corrosion process, so their formation is favored at lower temperatures. Although temperature influences inhibition efficiency [12–15], in this case, a decrease in solution temperature will increase the amount of dissolved CO2 [44] available to react with La3+ cations; therefore, its inhibition efficiency will not be affected in a significant way. In addition, for each La2(CO3)3 molecule formed, three moles of C are captured, unlike the formation of FeCO3, whose ratio is 1:1. The formation and precipitation of lanthanum carbonate increases both the adsorption and hydration of CO2, thus favoring a CO2-capture process and transforming it into a more stable product with low solubility [45]. This reduces the corrosiveness of the electrolyte, favoring the formation of a barrier and thereby reducing the corrosion rate of carbon steel. When CO2 capture occurs by its dissolution in water, it is also called a CO2 mineralization process [41,46].

Furthermore, lanthanum carbonate has a higher free energy of formation and greater E–pH stability range than iron carbonate [47]. The formation of iron carbonate is favored at temperatures and times greater than those evaluated here [4]. In this way, the for- mation and precipitation of a barrier layer of lanthanum carbonate guarantees a greater protective capacity.

3. Materials and Methods

As a study material, 1018 carbon steel specimens with dimensions 10 × 10 × 5 mm were used (1 cm2 reaction area). Using the spot-welding technique, a copper conductor wire was welded to one of the faces of the specimens, and in this condition, they were encapsulated in epoxy resin. The encapsulated samples were roughened with abrasive paper from grade 120 to grade 600. Subsequently, they were washed with distilled water and ethanol, dried, and used immediately in the corrosion tests.

As corrosive medium, a solution of NaCl (3.5% by weight) saturated with CO2 at a temperature of 60 ◦C was used. The solution was saturated with CO2 for at least one hour before starting the tests. To maintain saturation, CO2 bubbling was maintained for the duration of the tests performed. Lanthanum chloride (LaCl3) was used as a corrosion inhibitor at concentrations of 0.0001 M, 0.0005 M, 0.001 M, 0.005 M, and 0.01 M. In all cases, the inhibitor was added to the corrosive medium one hour after the immersion of the working electrode. The inhibitor was added in its pure state, and its homogenization in the electrolyte was carried out with stirring for 5–10 s.

The electrochemical tests were carried out in a three-electrode cell where the encap- sulated specimens were the working electrodes, the reference electrode was a saturated calomel electrode, and a graphite bar was used as a counter electrode. The electrochemical tests carried out were potentiodynamic polarization curves, open circuit potential (OCP)

Molecules 2022, 27, 5209

16 of 18

measurements, linear polarization resistance (RPL), and electrochemical impedance spec- troscopy (EIS). Before each test, the working electrode was immersed in the electrolyte for 15 min to achieve a steady state. Electrochemical measurements were performed for 50 h with a GAMRY potentiostat/galvanostat (model 1000).

The potentiodynamic polarization curves were obtained by polarizing the working electrode ±300 mV with respect to the corrosion potential at a scanning speed of 1 mV/s. OCP measurements were made at hourly intervals. RPL measurements were made by polarizing the working electrode ±10 mV with respect to its open-circuit potential at hourly intervals. EIS measurements were obtained by applying to the working electrode an amplitude perturbation of 10 mV (AC) with respect to the open-circuit potential over a frequency range of 100 kHz to 0.01 Hz.

The inhibition efficiency was calculated according to the following expression (Rpi = resistance to polarization in the presence of an inhibitor, Rpb = resistance to po- larization in the absence of an inhibitor):

E(%) = Rp

i

􏰌Rpi −Rpb􏰍

× 100, (17)

The surfaces of the samples were analyzed by SEM-EDS with an acceleration voltage of 20 kV, and by X-ray diffraction in the range of 10◦ ≤ 2θ ≤ 90◦ with a step of 0.003◦ and a time of 320 s per step.

4. Conclusions

Electrochemical studies carried out show that lanthanum chloride shows a high sweet corrosion inhibition capacity at concentrations as low as 1 mM. Its inhibition efficiency is greater than 95% and is greater than that observed in CO2-free electrolytes. Its addition to the electrolyte caused a rapid increase in the OCP and RPL values due to a decrease in the electrolyte corrosivity due to the capture of dissolved CO2. At higher concentrations, its inhibition efficiency tends to decrease due to the increase in the concentration of Cl− ions. Electrochemical impedance studies showed that the precipitation and deposition of lanthanum carbonate causes an increase in the capacitive response of the carbon steel surface and therefore, an increase in the charge transfer resistance.

Unlike the classical inhibition mechanisms, where the inhibitor molecules are adsorbed on the metal surface or precipitate on it by reacting with the OH− ions generated at the cathodic sites, in this study, it was found that the La3+ cations react with CO2 dissolved forming a barrier layer on the metal surface. La3+ cations act by a CO2 capture process that interrupts the classic route of the sweet corrosion mechanism, unlike organic inhibitors, whose inhibition mechanism is based on their adsorption capacity on the metal surface.

Author Contributions: Conceptualization, J.P.-C.; formal analysis, J.P.-C., J.C., L.M.M.-d.-l.-E. and A.N.; investigation, J.P.-C., J.C., L.M.M.-d.-l.-E. and A.N.; methodology, J.C., L.M.M.-d.-l.-E. and A.N.; supervision, J.P.-C.; writing—review and editing, J.P.-C. All authors have read and agreed to the published version of the manuscript.

Funding: This research received no external funding. Institutional Review Board Statement: Not applicable. Informed Consent Statement: Not applicable.Data Availability Statement: Not applicable.

Conflicts of Interest: The authors declare no conflict of interest.

Molecules 2022, 27, 5209 17 of 18

References

Kahyarian, A.; Brown, B.; Nesic, S. The Unified Mechanism of Corrosion in Aqueous Weak Acids Solutions: A Review of the Recent Developments in Mechanistic Understandings of Mild Steel Corrosion in the Presence of Carboxylic Acids, Carbon Dioxide, and Hydrogen Sulfide. Corrosion 2020, 6, 268–278. [CrossRef]

Kahyarian, A.; Nesic, S. On the mechanism of carbon dioxide corrosion of mild steel: Experimental investigation and mathematical modeling at elevated pressures and nonideal solutions. Corros. Sci. 2020, 173, 108719. [CrossRef]

Wright, R.F.; Brand, E.R.; Ziomek-Moroz, M.; Tylczak, J.H.; Ohodnicki, P.R., Jr. Effect of HCO−3 on electrochemical kinetics of carbon steel corrosion in CO2-saturated brines. Electrochim. Acta 2018, 290, 626–638. [CrossRef]

Sk, M.H.; Abdullah, A.M.; Ko, M.; Ingham, B.; Laycock, N.; Arul, R.; Williams, D.E. Local supersaturation and the growth of protective scales during CO2 corrosion of steel: Effect of pH and solution flow. Corros. Sci. 2017, 126, 26–36. [CrossRef]

Barker, R.; Burkle, D.; Charpentier, T.; Thompson, H.; Neville, A. A review of iron carbonate (FeCO3) formation in the oil and gas industry. Corros. Sci. 2018, 142, 312–341. [CrossRef]

Verma, C.; Quraishi, M.A.; Ebenso, E.E. A Review on Ammonia Derivatives as Corrosion Inhibitors for Metals and Alloys. In Sustainable Ammonia Production, Green Energy and Technology; Inamuddin Boddula, R., Asiri, A.M., Eds.; Springer: Cham, Switzerland, 2020. [CrossRef]

Godavarthi, S.; Porcayo-Calderon, J.; Casales-Diaz, M.; Vazquez-Velez, E.; Neri, A.; Martinez-Gomez, L. Electrochemical Analysis and Quantum Chemistry of Castor Oil-Based Corrosion Inhibitors. Curr. Anal. Chem. 2016, 12, 476–488. [CrossRef]

Porcayo-Calderon, J.; Rivera-Muñoz, E.M.; Peza-Ledesma, C.; Casales-Diaz, M.; Martínez de la Escalera, L.M.; Canto, J.; Martinez-Gomez, L. Sustainable Development of Palm Oil: Synthesis and Electrochemical Performance of Corrosion Inhibitors. J. Electrochem. Sci. Technol. 2017, 8, 133–145. [CrossRef]

Reyes-Dorantes, E.; Zuñiga-Díaz, J.; Quinto-Hernández, A.; Porcayo-Calderon, J.; Gonzalez-Rodriguez, J.G.; Pedraza-Basulto, G.K.; Martínez-Gomez, L. Rice Bran as Source for the Synthesis of Imidazoline-type Inhibitors: Synthesis and Corrosion Performance. Int. J. Electrochem. Sci. 2018, 13, 101–118. [CrossRef]

Abd El-Lateef, H.M.; El-Beltagi, H.S.; Mohamed Mohamed, M.E.; Kandeel, M.; Bakir, E.; Toghan, A.; Shalabi, K.; Tantawy, A.H.; Khalaf, M.M. Novel Natural Surfactant-Based Fatty Acids and Their Corrosion-Inhibitive Characteristics for Carbon Steel-Induced Sweet Corrosion: Detailed Practical and Computational Explorations. Front. Mater. 2022, 9, 843438. [CrossRef]

Shahzad, K.; Sliem, M.H.; Shakoor, R.A.; Radwan, A.B.; Kahraman, R.; Umer, M.A.; Manzoor, U.; Abdullah, A.M. Electrochemical and thermodynamic study on the corrosion performance of API X120 steel in 3.5% NaCl solution. Sci. Rep. 2020, 10, 4314. [CrossRef]

Zhang, G.; Chen, C.; Lu, M.; Chai, C.; Wu, Y. Evaluation of inhibition efficiency of an imidazoline derivative in CO2-containing aqueous solution. Mater. Chem. Phys. 2007, 105, 331–340. [CrossRef]

AI-Mayouf, A.M.; Al-Ameery, A.K.; Al-Suhybani, A.A. Inhibition of Type 304 Stainless Steel Corrosion in 2 M Sulfuric Acid by Some Benzoazoles-Time and Temperature Effects. Corrosion 2001, 57, 614–620. [CrossRef]

Popova, A.; Sokolova, E.; Raicheva, S.; Christov, M. AC and DC study of the temperature effect on mild steel corrosion in acid media in the presence of benzimidazole derivatives. Corros. Sci. 2003, 45, 33–58. [CrossRef]

Allachi, H.; Chaouket, F.; Draoui, K. Corrosion inhibition of AA6060 aluminium alloy by lanthanide salts in chloride solution. J. Alloys Compd. 2009, 475, 300–303. [CrossRef]

Mohammedi, D.; Ismail, F.; Rehamnia, R.; Bensalem, R.; Savadogo, O. Corrosion behaviour of steel in the presence of rare earth salts: Synergistic effect. Corros. Eng. Sci. Technol. 2015, 50, 633–638. [CrossRef]

Yanhua, Z.; Jia, Z.; Yongsheng, Y.; Xianguang, Z. Research on anti-corrosion property of rare earth inhibitor for X70 steel. J. Rare Earths 2013, 31, 734–740.

Bernal, S.; Botana, F.J.; Calvino, J.J.; Marcos, M.; Perez-Omil, J.A.; Vidal, H. Lanthanide salts as alternative corrosion inhibitors. J. Alloys Compd. 1995, 225, 638–641. [CrossRef]

Davó, B.; de Damborenea, J.J. Use of rare earth salts as electrochemical corrosion inhibitors for an Al–Li–Cu (8090) alloy in 3.56% NaCl. Electrochim. Acta 2004, 49, 4957–4965. [CrossRef]

Ho, D.; Brack, N.; Scully, J.; Markley, T.; Forsyth, M.; Hinton, B. Cerium Dibutylphosphate as a Corrosion Inhibitor for AA2024-T3 Aluminum Alloys. J. Electrochem. Soc. 2006, 153, B392–B401. [CrossRef]

Allachi, H.; Chaouket, F.; Draoui, K. Protection against corrosion in marine environments of AA6060 aluminium alloy by cerium chlorides. J. Alloys Compd. 2010, 491, 223–229. [CrossRef]

Dastgheib, A.; Attar, M.M.; Zarebidaki, A. Evaluation of Corrosion Inhibition of Mild Steel in 3.5 wt% NaCl Solution by Cerium Nitrate. Met. Mater. Int. 2020, 26, 1634–1642. [CrossRef]

Martinez de la Escalera, D.M.; Ramos-Hernandez, J.J.; Porcayo-Palafox, E.; Porcayo-Calderon, J.; Gonzalez-Rodriguez, J.G.; Martinez-Gomez, L. Effect of Nd3+ Ion Concentration on the Corrosion Resistance of API X70 Steel in Chloride-Rich Environments. Adv. Mater. Sci. Eng. 2018, 2018, 9328317. [CrossRef]

Porcayo-Calderon, J.; Ramos-Hernandez, J.J.; Porcayo-Palafox, E.; Martinez de la Escalera, L.M.; Canto, J.; Gonzalez-Rodriguez, J.G.; Martinez-Gomez, L. Sustainable Development of Corrosion Inhibitors from Electronic Scrap: Synthesis and Electrochemical Performance. Adv. Mater. Sci. Eng. 2019, 2019, 6753658. [CrossRef]

Vazquez-Ramirez, R.; Salinas-Solano, G.; Porcayo-Calderon, J.; Gonzalez-Rodriguez, J.G. Use of (Nd, Pr) Sulfates Obtained from Electronic Scrap as Corrosion Inhibitors for a C-Mn Steel in 3.5 NaCl. Int. J. Corros. Scale Inhib. 2021, 10, 602–617. [CrossRef]

Molecules 2022, 27, 5209 18 of 18

Chen, X.-B.; Cain, T.; Scully, J.R.; Birbilis, N. Technical Note: Experimental Survey of Corrosion Potentials for Rare Earth Metals Ce, Er, Gd, La, and Nd as a Function of pH and Chloride, Concentration. Corrosion 2013, 70, 323–328. [CrossRef]

Arenas, M.A.; Conde, A.; de Damborenea, J.J. Cerium: A suitable green corrosion inhibitor for Tinplate. Corros. Sci. 2002, 44, 511–520. [CrossRef]

Bethencourt, M.; Botana, F.J.; Calvino, J.J.; Marcos, M.; Rodriguez-Chacon, M.A. Lanthanide compounds as environmentally- friendly corrosion inhibitors of aluminium alloys: A review. Corros. Sci. 1998, 40, 1803–1819. [CrossRef]

El Miligy, A.A.; Geana, D.; Lorenz, W.J. A theoretical treatment of the kinetics of iron dissolution and passivation. Electrochim. Acta 1975, 20, 273–281. [CrossRef]

Nam, N.D.; Somers, A.; Mathesh, M.; Seter, M.; Hinton, B.; Forsyth, M.; Tan, M.Y.J. The behaviour of praseodymium 4-hydroxycinnamate as an inhibitor for carbon dioxide corrosion and oxygen corrosion of steel in NaCl solutions. Corros. Sci. 2014, 80, 128–138. [CrossRef]

Arenas, M.A.; de Damborenea, J.J. Growth mechanisms of cerium layers on galvanised steel. Electrochim. Acta 2003, 48, 3693–3698. [CrossRef]

Amin, M.A.; Ahmed, M.A.; Arida, H.A.; Kandemirli, F.; Saracoglu, M.; Arslan, T.; Basaran, M.A. Monitoring corrosion and corrosion control of iron in HCl by non-ionic surfactants of the TRITON-X series—Part III. Immersion time effects and theoretical studies. Corros. Sci. 2011, 53, 1895–1909. [CrossRef]

Al-Otaibi, M.S.; Al-Mayouf, A.M.; Khan, M.; Mousa, A.A.; Al-Mazroa, S.A.; Alkhathlan, H.Z. Corrosion inhibitory action of some plant extracts on the corrosion of mild steel in acidic media. Arab. J. Chem. 2014, 7, 340–346. [CrossRef]

Bahgat Radwan, A.; Sliem, M.H.; Okonkwo, P.C.; Shibl, M.F.; Abdullah, A.M. Corrosion inhibition of API X120 steel in a highly aggressive medium using stearamidopropyl dimethylamine. J. Mol. Liq. 2017, 236, 220–231. [CrossRef]

Usman, B.J.; Umoren, S.A.; Gasem, Z.M. Inhibition of API 5L X60 steel corrosion in CO2-saturated 3.5% NaCl solution by tannic acid and synergistic effect of KI additive. J. Mol. Liq. 2017, 237, 146–156. [CrossRef]

Li, H.; Li, D.; Zhang, L.; Baia, Y.; Wang, Y.; Lu, M. Fundamental aspects of the corrosion of N80 steel in a formation water system under high CO2 partial pressure at 100 ◦C. RSC Adv. 2019, 9, 11641–11648. [CrossRef]

Yasakau, K.A.; Zheludkevich, M.L.; Lamaka, S.V.; Ferreira, M.G.S. Mechanism of Corrosion Inhibition of AA2024 by Rare-Earth Compounds. J. Phys. Chem. B 2006, 110, 5515–5528. [CrossRef]

Matter, E.A.; Kozhukharov, S.; Machkova, M.; Kozhukharov, V. Comparison between the inhibition efficiencies of Ce(III) and Ce(IV) ammonium nitrates against corrosion of AA2024 aluminum alloy in solutions of low chloride concentration. Corros. Sci. 2012, 62, 22–33. [CrossRef]

Hu, T.; Shi, H.; Wei, T.; Liu, F.; Fan, S.; Han, E.-H. Cerium tartrate as a corrosion inhibitor for AA 2024-T3. Corros. Sci. 2015, 95, 152–161. [CrossRef]

Zhang, L.J.; Zhang, Z.; Zhang, J.Q.; Cao, C.N. The study of the La(NO3)3 inhibition on X70 pipeline steel in 3.0(wt.%) NaCl solution. Mater. Corros. 2005, 56, 630–635. [CrossRef]

Hassas, B.V.; Rezaee, M.; Pisupati, S.V. Precipitation of rare earth elements from acid mine drainage by CO2 mineralization process. Chem. Eng. J. 2020, 399, 125716. [CrossRef]

Pei, S.-L.; Pan, S.-Y.; Li, Y.-M.; Chiang, P.-C. Environmental benefit assessment for the carbonation process of petroleum coke fly ash in a rotating packed bed. Environ. Sci. Technol. 2017, 51, 10674–10681. [CrossRef] [PubMed]

Lopez, M.; Porcayo-Calderon, J.; Casales-Diaz, M.; Carrillo, I.; Canto, J.; Martinez de la Escalera, L.M.; Cuevas-Arteaga, C.; Regla, I.; Melgoza-Aleman, R.M.; Martinez-Gomez, L. Internal Corrosion Solution for Gathering Production Gas Pipelines Involving Palm Oil Amide Based Corrosion Inhibitors. Int. J. Electrochem. Sci. 2015, 10, 7166–7179.

Li, X.; Peng, C.; Crawshaw, J.; Maitland, G.; Trusler, J.M. The pH of CO2-saturated aqueous NaCl and NaHCO3 solutions at temperatures between 308 K and 373 K at pressures up to 15 MPa. Fluid Phase Equilibria 2018, 458, 253–263. [CrossRef]

Kim, P.; Anderko, A.; Navrotsky, A.; Riman, R.E. Trends in Structure and Thermodynamic Properties of Normal Rare Earth Carbonates and Rare Earth Hydroxycarbonates. Minerals 2018, 8, 106. [CrossRef]

Sanna, A.; Uibu, M.; Caramanna, G.; Kuusik, R.; Maroto-Valer, M.M. A review of mineral carbonation technologies to sequester CO2. Chem. Soc. Rev. 2014, 43, 8049–8080. [CrossRef]

Brookins, D.G. Eh-pH Diagrams for Geochemistry; Springer: Berlin/Heidelberg, Germany, 1988; ISBN 978-3-642-73093-1. [CrossRef]

Written by

CORROSION Y PROTECCION

Tags

Next Inhibition of X52 Corrosion in CO2-Saturated Brine by a Dialkyl-Diamide from Coffee Bagasse Oil